Search Results

To give the wear-resistance to titanium intake valves by simple oxidation treatment, oxidation condition and microstructure of Ti-6Al-4V bars were studied. The wear test using a valve simulator shows that the wear of the face oxidized at 820°C for 1 and 4h in air is superior to that of ferrous valves. The best micro-structure of Ti-6Al-4V bar is an acicular structure with the prior β grain size of 30 to 60 μ m in average, which prevents distortion during the oxidation treatment and has excellent mechanical properties.

Improvement of material characteristic values, adjustment of forming conditions as well as introduction of new forming technics are necessary to promote wide application of aluminum alloy sheets into automotive parts. 5000 series and 6000 series aluminum alloy sheets are concerned about the relationship between material characteristic values and fundamental forming ability required to apply them to automobile body parts as well as the effect of lubricant on their formability. The hardening parameters, n values, of them are larger than those of cold-rolled steel sheets. However, the r values and the local elongations are extremely small. The improvement of stretch formability owing to increase of n value is smaller than that of the steel sheets. Inferior deep drawability of the aluminum alloy sheets is due to low fracture resistance force caused by low r value.

Carburizing heat treatment is one of the automobile component manufacturing steps, which consumes a large amount of energy. Raising the carburizing temperature can shorten the carburizing time and save the energy, but involves the risks of grain coarsening and attendant property deterioration. The authors have clarified the precipitation behavior of aluminum nitride (A1N) in the automobile gear manufacturing process and the optimum precipitation of A1N in as-rolled steel bars to prevent the grain coarsening. Through the application of the controlled rolling technique to ensure the optimum precipitation of A1N in continuously cast steel of uniform chemical composition, the authors have substantially saved energy while maintaining high quality, and developed a high-temperature carburizing steel expected to minimize and stabilize quenching strains.

We have taken notice of Zn-Fe alloy electroplating with an eye to developing new corrosion-resistant steel sheets for automotive use with both cosmetic corrosion resistance and perforating corrosion resistance, and as a result of investigations into its paintability and corrosion resistance over the whole range of its compositions, we have come to a conclusion that steel sheets with two-layer Zn-Fe alloy electroplating that consists of a thin upper layer with a 75 to 85% Fe content and a lower layer with a 10 to 20% Fe content is the best choice.

Eight kinds of the spot-welded test specimens were studied to obtain the basic fatigue data on steel sheets for car bodies. Analytical methods such as the strain amplitude at outside and inside plates close to the nugget, the maximum nominal stress and Kθmax criteria of fracture mechanics were used. The authors propose that the ratio of strains at two points around the nugget can provide evaluation of the bending load and estimation of the fatigue strength.

Vibration Damping Steel Sheet (VDSS) for automotive use, which has a three layer structure of steel/viscoelastic resin/steel, has been studied. For automotive body panels, VDSS is required to have not only high vibration damping capability but also other properties such as bonding strength, formability, weldability and durability. In this research, the effect of resin layer on these properties was studied. It is found that VDSS which satisfies these properties can be made from thermosetting resin involving metal particles.

In order to examine the compatibility of improvement of crashworthiness with weight-saving of automobiles by using high strength steel, a combination analysis of Finite Element Method and Dynamic Mechanical Properties has been established. The material properties used in this analysis have been measured by “one bar method” high velocity tensile tests, which can examine the deformation behaviour of materials at an actual crash speed range (∼55km/h). As for the accuracy of this system, comparison between experiments and FEM simulation both of this test machine and other high-velocity-tensile-test machines have clarified the feature of one bar method and the metallurgical features of high velocity deformation. It was confirmed that the stress-strain curve measured by the one bar method agreed with that measured by the modified Split Hopkinson pressure bar method.

The Strategic Alliance for Steel Fuel Tanks (SASFT), an international group of steel producers and manufacturing companies, recently completed a major corrosion study of various steel ‘systems’ for automobile fuel tanks. The ten steel systems included low carbon steels (either pre-painted or post-painted with protective coatings) and stainless steels. The 2-year corrosion test program included testing in salt solutions to simulate road environments for the exterior of a fuel tank. Special test specimens were designed to represent a manufactured tank. The external tests used were the Neutral Salt Spray test (ASTM B117) with exposures up to 2000 hours and the Cyclic Corrosion test (SAE J2334) with exposures up to 120 and 160 cycles to represent vehicle lives of 15 years and 20 years, respectively. Additionally, the resistance to an aggressive ethanol-containing fuel (internal tank corrosion) was assessed by using uniquely designed drawn cups of the various steel systems.